 TERMOGRAF TCS can be combined with various interlayer materials to improve performance and handling. Carbon Steel Tanged Metal, Aluminum and SS316L/SS304, Nickel foil are available. |
- FGS is pure graphite sheet without insertment
- ASS316 is graphite sheet reinforced by adhesive 0.05MM SS316 insert.
- ASS304 is graphite sheet reinforced by adhesive 0.05MM SS304insert.
- TSS316 is graphite sheet reinforced by tanged 0.1MM SS316 insert
- TTSS is three layer graphite sheets reinforced by two layers of tanged SS
- TSS304 is graphite sheet reinforced by tanged 0.1MM SS304 insert
- TCS is graphite sheet reinforced by tanged 0.2-0.25MM carbon steel
- MSS316 is graphite sheet reinforced by 24 mesh wire SS316 insert
- MSS304 is graphite sheet reinforced by 24 mesh wire SS304 insert
- AGN is graphite sheet reinforced by adhesive nickel foil insert
Specification:
| Density | 0.7-1.6g/cm3 |
| Thickness | 0.5MM-6.0MM |
| Size | 1000MM X 1000MM; 1500MM X 1500MM;
1000MM X 2000MM; 1500MM X 2000MM 1500MM X 3000MM; 1000MM X 3000MM 610MM X 610MM; 1270MM X 1270MM |
Technical Data.
| Maximum Operating Temperature1 | 450 | ?aC | |
| Compressibility ASTM F36A | 33 – 38 | % | |
| Recovery ASTM F36A (min) | 13 – 18 | % | |
| Flexealing hot compression test 50 MPa 300?aC | |||
| Thickness decrease 23?aC | 40 | % | |
| Thickness decrease 300?aC | 1.5 | % | |
| Gas leakage DIN 3535/6 | <0.8 | ml/min | |
| Stress Relaxation DIN 52913 (16h, 300?aC) | 48 | MPa | |
| Thickness increase ASTM F146 | |||
| ASTM Oil No. 3 (5h/150?aC) | 5 – 10 | % | |
| ASTM Fuel B (5h/23?aC) | 4 – 6 | % | |
| Ethylene glycol/water (1:1) (5h/150?aC) | 3 – 5 | % | |
| Density (Standard) | 1.0 | g/cm2 | |
| Chloride Content (graphite layer) | max 40 | ppm | |
| Maximum allow. surface stress @ 450?aC | 150 | MPa | |
| Graphite Purity | min 98 | % | |
Note: